Adhesion to a lithium disilicate glass ceramic etched with hydrofluoric acid at distinct concentrations

Abstract This study evaluated the effect of different hydrofluoric acid (HF) concentrations on the bond strength between a lithium disilicate-based glass ceramic and a resin cement. Eighty ceramic-blocks (12×7×2 mm) of IPS e.Max CAD (Ivoclar Vivadent) were produced and randomly assigned to 8 groups, considering 2 study factors: HF concentration in 4 levels, i.e., 1% (HF1), 3% (HF3), 5% (HF5), and 10% (HF10), and storage in 2 levels, i.e., baseline (tests were performed 24 h after cementation), and aged (storage for 150 days + 12,000 thermal-cycles at 5°C and 55°C). Acid etching (20 s) was performed, followed by washing, drying, and silanization. Four resin cement cylinders (ϕ= 0.96 mm) were built-up from starch matrices on each ceramic sample (n= 40). Additional ceramic samples were etched and analyzed for contact angle, micro-morphology, and roughness. In baseline condition (without aging), the HF3, HF5, and HF10 groups showed similar bond strength values (13.9 - 15.9 MPa), and HF1 (11.2 MPa) presented lower values than HF5, being that statistically different (p= 0.012). After aging, all the mean bond strengths statistically decreased, being that HF3, HF5, and HF10 (7.8 - 11 MPa) were similar and higher than HF1 (1.8 MPa) (p= 0.0001). For contact angle, HF3, HF5, and HF10 presented similar values (7.8 - 10.4°), lower than HF1 and CTRL groups. HF5 and HF10 presented rougher surfaces than other conditions. For better bond strength results, the tested ceramic may be etched by HF acid in concentrations of 3%, 5%, and 10%.

Resumo Este estudo avaliou o efeito de diferentes concentrações de ácido fluorídrico (HF) na resistência de união entre uma cerâmica vítrea à base de dissilicato de lítio e um cimento resinoso. Oitenta blocos cerâmicos (12×7×2 mm) de IPS e.Max CAD (Ivoclar Vivadent) foram produzidos e distribuídos aleatoriamente em 8 grupos, considerando 2 fatores de estudo: concentração de HF em 4 níveis, isto é, 1% (HF1), 3% (HF3), 5% (HF5), e 10% (HF10), e armazenamento em 2 níveis, isto é, condição inicial (testes foram realizados 24 h após a cimentação), e envelhecidos (150 dias de armazenamento + 12.000 ciclos térmicos a 5°C e 55°C). Condicionamento ácido (20 s) foi realizado, seguido por lavagem, secagem e silanização. Quatro cilindros de cimento resinoso (ϕ= 0.96 mm) foram construídos a partir de matrizes de amido em cada amostra cerâmica (n= 40). Amostras cerâmicas adicionais foram condicionadas e analisadas quanto ao ângulo de contato, micro-morfologia e rugosidade. Na condição inicial (sem envelhecimento), os grupos HF3, HF5, e HF10 mostraram valores de resistência de união similares (13.9 - 15.9 MPa), e HF1 apresentou valores menores que HF5, sendo estatisticamente diferente (p= 0.012). Após o envelhecimento, todas as médias de resistência de união diminuíram estatisticamente, sendo que HF3, HF5 e HF10 foram similares e maiores que HF1 (p= 0.0001). Para o ângulo de contato, HF3, HF5 e HF10 apresentaram valores similares (7.8 - 10.4°), menores que os grupos HF1 e CTRL. HF5 e HF10 apresentaram superfícies mais rugosas que as outras condições. Para melhores resultados de resistência de união, a cerâmica testada pode ser condicionada com ácido fluorídrico nas concentrações de 3%, 5% e 10%.

Tratamento estético de lesões não cariosas: série de casos / Aesthetic treatment of non-carious lesions: a case series

As lesões não cariosas têm sido frequentemente motivo de queixa de pacientes odontológicos, sobretudo quando elas têm implicações estéticas. A etiologia desses desgastes é multifatorial, sendo proveniente de processos mecânicos, que determinam desgaste por atrição, abrasão e abfração, e químicos, como a erosão. O aumento da incidência de lesões desse tipo direcionou maior atenção ao diagnóstico multidisciplinar e levou ao desenvolvimento de novas opções de terapias restauradoras minimamente invasivas. A presente série de casos de busca apresentar uma opção conservadora e multidisciplinar, desde o diagnóstico ao tratamento e proservação de desgastes dentários de diversas etiologias, com especial atenção para a estética e saúde geral do paciente...

Non-carious lesions have increasingly become a cause of patients complaint, especially when aesthetic implications are involved. The etiology of non-carious tooth wear is multifactorial. Mechanical processes which produce wear by attrition, abrasion and abfraction, and chemicals factors which produce tooth loss by erosion. The increasing incidence of these lesions led to a greater attention to multidisciplinary diagnosis and the development of new options of minimally invasive restorative therapies. This case series aims to presents a conservative and multidisciplinary approach, from diagnosis to treatment and proservation of tooth wear of various etiologies, with special attention to the aesthetics and patient’s general health...